Lihuayi Weiyuan PC Wy-106br Polycarbonate Mfr 6

• Feature: Transparent, High Impact, Heat-Resistant
• CAS No.: 25037-45-0
• Formula: (C8h8)N
• Model NO.: Lihuayi Weiyuan PC WY-106BR
• EINECS: 500-044-8
• Material: Polycarbonates/PC
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Extrusion
• Color: White
• Loading Port: Qingdao
• MOQ: 1X40FT
• HS: 39074000
• Mfr: 6
• Transport Package: Plastic Bag
• Specification: In 25kg/bag, 27MT/40GP with pallets
• Trademark: Lihuayi Weiyuan
• Origin: China
• HS Code: 39074000

Product Description

Polycarbonate (PC) is an engineering thermoplastic renowned for its exceptional impact resistance (virtually unbreakable), high optical clarity (up to 90% light transmission), and thermal stability (service temp: -135°C). Derived from bisphenol-A monomers, it withstands harsh environments while remaining 200x stronger than glass. Dominant applications include bullet-resistant windows, electronic housings (phones/laptops), automotive headlights, and medical devices. PC processes via injection molding/extrusion but requires pre-drying to prevent hydrolysis. Though costlier than commodity plastics, its unique blend of durability, transparency, and flame retardancy (UL94 V-0 grade) makes it irreplaceable in high-performance sectors. BPA-free variants address niche health concerns. 

Features

Medium to high viscosity and excellent demolding performance.

Applications

Widely used in electronic device casings (like phones and computers), automotive parts (such as lamp covers), optical products (e.g., spectacle lenses), medical device components, etc.

Packaging

In 25kg/bag,27MT/40GP with pallets

Property

Unit

Test Condition

Result

Test Method

Melt Mass-Flow Rate

g/10min

300ºC,1.2 Kg

6

ASTM D1238

Haze

%

3.2mm

0.4

ASTM D1003

Transmittance

%

3.2mm

89

ASTM D1003

Mass Density

/

23ºC

1.2

ASTM D792

Hardness

L

/

100.4

ASTM D785

Tensile Strength

Kg/cm 2

6 mm/min(Yield)

690

ASTM D638

Tensile Elongation

%

6 mm/min

112

ASTM D638

Flexural Strength

MPa

1.3 mm/min

96.3

ASTM D790

Flexural Modulus

100000 Kg/cm 2

1.3 mm/min

2.5

ASTM D790

Izod Impact Strength

Kg-cm/cm

3.2 mm, 23ºC

83

ASTM D256(Notched)

Vicat Softening Temp

ºC

1 Kg,120 ºC/hr

152

ASTM D1525

Heat Distortion Temp

ºC

132ºC×8 hours Loading 4.6 kg/cm 2

150.0

ASTM   D648(Annealed)

UL Flammability

/

/

V-2

UL 94

Formed shrinkage

%

Parallel Direction

0.7

ISO 294-4