LLDPE Film Grade Exxonmobil 1002bu, Mfr=1

• Feature: Polymer
• CAS No.: 9002-88-4
• Formula: (C2h4)N
• EINECS: 618-339-3
• Material: Polyethylene/PE
• Usage: General Plastics
• Model NO.: 1002BU
• Plastic Properties After Heated: Thermosetting Plastic
• Plastic Forming Method: Film Pressure
• Color: White
• Processing: Oil Base
• Mfr: 1
• Transport Package: 24.75mt/40gp with Pallet
• Specification: 25kg bag
• Trademark: Exxonmobil
• Origin: USA
• HS Code: 3901402090
• Production Capacity: 2 Million Tons/Year

Product Description

 

Description:

This high molecular weight, hexene copolymer is tailored for blown film applications that require:Toughness and durability; Good processability; Good blending characteristics with HDPE HMW resins.

Applications:

Typical applications for HHM TR-144 include:T-shirt bags; Multi-wall liners; Trash bags.

Packaging:
In 25kg bag, 26-28MT in one 40HQ.

 

No.	Properties	Value (SI Units)	Method
01	Density	0.946 g/cm3	ASTM D1505
02	Melt Index, Condition 190°C / 2.16 kg	0.18 g/10 min	ASTM D1238
03	Brittleness Temperature, Type A clamp, Type I specimen	<-75°C	ASTM D746
04	ESCR,  Condition B (100% Igepal), F50	>1000 hrs	ASTM D1693
05	Flexural Modulus, Tangent - 16:1 span:depth, 12.7 mm/min	1150 MPa	ASTM D790
06	Dart Drop (66 cm)	90 g	ASTM D1709
07	Tensile Strength at Yield, 50.8 mm/min MD	24 MPa	ASTM D882
08	Tensile Strength at Yield, 50.8 mm/min TD	26 MPa	ASTM D882
09	Elongation at Break, 50.8 mm/min MD	480%	ASTM D882
10	Elongation at Break, 50.8 mm/min TD	640%	ASTM D882
11	Elmendorf Tear Strength, MD	19 g	ASTM D1922
12	Elmendorf Tear Strength, TD	270 g	ASTM D1922