Pph Yarn Grade Daxie 1102K, Mi=2.96

• Feature: Polymer
• CAS No.: 9003-07-0
• Formula: (C3h6)N
• Model NO.: 1102K
• EINECS: 202-316-6
• Material: Polypropylene/PP
• Usage: General Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: PP Raffia
• Color: White
• Raw Materilas: Oil
• Mi: 3.4±1.0
• Transport Package: PE Bag
• Specification: 25kg bag
• Trademark: cnooc
• Origin: China
• HS Code: 3902100039
• Production Capacity: 1 Million Tons/Year

Product Description

Description:
Polypropylene(PP) , a kind of non-toxic,odorless, tasteless opalescent polymer with high crystallization, the melting point among 164- 170C, the density among 0.90-0.91g/cm3 , the molecular weight is about 80,000- 150,000. PP is   one of the lightest plastic of all varieties at present, particularly stable in water, with a water absorption rate in water for 24 hours is only 0.01%.

Application:
Polypropylene 1102K adopts the Unipol gas-phase fluidized bed process of US Grace, it is widely be used to produce woven bags, fiber,
applicable for textile,jumbo bags,carpet and backing etc.

Packaging:
In 25kg bag, 16MT in one 20fcl without pallet or 26-28MT in one 40HQ without pallet or 700kg jumbo bag, 26-28MT in one 40HQ without pallet.

 

No.	ITEM	UNIT	INDEX	TEST METHOD
01	Melt mass flow(MFR)    Standard value	g/10min	3.4	GB/T 3682. 1-2018
02	Melt mass flow(MFR)    Deviation value	g/10min	± 1.0	GB/T 3682. 1-2018
03	Color Pellet	Per/kg	0	SH/T 1541-2006
04	Black Pellet	Per/kg	0	SH/T 1541-2006
05	Dust	%(m/m)	≤0.05	GB/T 9345. 1-2008
06	Tensile yield stress	Mpa	≥ 29.0	GB/T 1040.2-2006
07	Tensile fracture stress	Mpa	≥ 15.0	GB/T 1040.2-2006
08	Tensile fracture nominal stress	%	≥ 150	GB/T 1040.2-2006
09	Yellow color Index	%	≤ 4	HG/T 3862-2006